TWO-Component Polysulfide Sealant For Insulating Glass
Two-component room cured polysulfide sealant, specifically designed for the manufacturing of insulating glass units used for window and door as well as for edge frame curtain wall system.
DESCRIPTION/APPLICATIONS
Two-component room cured polysulfide sealant, specifically designed for the manufacturing of insulating glass units used for window and door as well as for edge frame curtain wall system. The sealant is sensitive to temperature and humidity while mixing. The higher temperature,the faster curing speed
TYPICAL PERFORMANCE
• Excellent adhesion to a wide range substrates including glass,aluminium alloy,and galvanized steel,stainless steel.· Excellent temperature stability:-60℃ to 180℃.
• High elasticity and strength
• Solvent free,primers are not required.
Technical indicators:
TEST ITEMS | TEST RESULT | |
Test Condition:14d placed at T(23±2)℃,(50±5)%RH | ||
Color | Component A (base):white | |
Component B(catalyst):black | ||
Mixture(A+B):black | ||
MIXING RATIO | 10:1(by weight) | |
APPLICATION TIME(23 ) | 20 mins, influenced by room conditions. | |
TACK-FREE TIME | 20-30 mins,depends on application time. | |
DENSITY | Com A[23℃] | approx. 1.83±0.02 [g/cm] |
Com B[23℃] | approx.1.53 [g/cm³ | |
VIsCOSITY | Com A[23℃] | 620 Pa.s |
Com B[23℃] | 100 Pa.s | |
FINAL HARDNESS(Shore A) | 45-50(After 14 days) | |
MOISTURE VAPOUR TRANSMISSION(MVTR) | 11 gr/m2.24hrs.2mm EN 1279/4 | |
GAS PERMEATION(Ar) | 6.63x10[gr/m2hrs EN 1279/4 | |
TENSILEADHESION STRENGTH | ≥1.0 MPa | |
VOLATILE CONTENT(A+B) | <1.0% | |
FOGGING | Without visual fogging |
Related Products
Horizontal Glass Washing and Drying Machine
Horizontal Glass Washing Machine
Glass Cantilever Crane
LJXJ300/ 500
Intelligent Glass Storage and Sorting System
Insulating Glass Storage Chip System
Automatic Jumbo Size Double Gas Filling Insulating Glass Production Line
Insulating Glass Machine