Silica Hot Repair and Mortar, China Silica Hot Repair and Mortar Supplier

Silica Hot Repair and Mortar - TY

Silica Hot Repair and Mortar For Sale, Most Competitive Price, Fast Delivery, Custom Service, Wholesale Silica Hot Repair and Mortar, Made in China, High Quality Products!, China Silica Hot Repair and Mortar, silica hot repairing mix Supplier, Manufacturer.

The silica hot repairing mix is used for hot repairing of silica brick crown top of glass furnace. The silica mortar used together with the hot repairing mix possesses the properties of high temperature resistance, corrosion resistance and high binding ability at normal temperature making the binding of silica brick with hot repairing mix easy.
? Directions for Use of Silica Mortar
1.Descriptions: silica mortar is mainly used for masonry of high quality silica bricks. Packed with paper bag outside, there is plastic moisture proof bag inside. Weight per bag is 25kg and there is one small bag of additives in each bag of mortar. The red sign on the front of the package is obvious, which is used to distinguish it from other bulk material during application.
2.Mixing sequence: the silica mortar is the fine powder (0.088mm). Put the mortar in to the mixer and spray the small bag of additives on the dry powder evenly, mix them for 3 to 5min. Next, put 32 to 35 per cent of clean water (tap water and water amount can be adjusted according to actual conditions) into it and continue mixing for 5 to 10min. The effect will be better if you put the mortar slurry static for 10min. Amount of agitation should be determined according to the capacity of mixer. But it must be used by the bag.
3.The mortar well mixed should be used as soon as possible for fear of loosing effectiveness.
4.Precautions: it is prohibited to put the additives into the water separately; it is prohibited to use acid industrial waste water to mix the slurry; operate strictly according to the requirements, or else it will influence the masonry quality and useful life of the mortar.

chemical compositions
SiO2≥ 96%
Al2O3≤ 0.8%
Fe2O3≤ 0.7%
physical properties
Sticking time : 1-3min
Bulk density: 2.1g/cm3
Granularity : ≥0.2mm ≤2%
＜0.074mm ≥60%
Refractoriness: 1710℃
Rupture (binding) strength (Mpa), after burnt at 110℃X24h ≥0.8 1400℃X3h ≥1.5

Get Quote

Zhengzhou Sunrise Refractory Co., Ltd.

Address: No.36, Fengchan Street, Jinshui District, Zhengzhou, Henan, China, 450000
Tel: +8637163838939
Zhengzhou Sunrise Refractory Co., Ltd. locates at centre China. The major railway intersection of Jingguang and Longhai is close to Zhengzhou Xinzheng International Airport. To expand its import and export business, Sunrise has established long-term business with dozens of customer all over the world and maintained good cooperation with them. Our main products are as follows: fused cast AZS 33#,36#,41#, glass furnace fireclay bottom block, mullite brick, zircon brick, alumina bubble brick, sillimanite brick, corundum brick, low porosity fireclay brick, high alumina brick, all kinds of glass furnace ramming masses, sealing materials, building fireclay, etc. Sunrise can offer the customer excellent service relating to the production line of the float glass, which includes the design and advisory of the furnace and the tin bath, the matching of the materials and its construction. The products made by our company have been used in more than 80 production lines of float glass and production line of glass products both at home and abroad. Sunrise conscientiously observes the government's line, policy, laws and regulations, follows the international trade practice, adheres to the principle of equality and mutual benefit, complies with contract and keeps the promise. BWTC upholds the principle of "combining industry with trade", "technology with trade" and "export with import", to serve its customer at home and abroad sincerely.