PVDF Color coated aluminum coil 1050 coating thickness 25 - 28 micron

?

Polyester Coatings (PE)
? ? PE (polyester) coatings exhibit an excellent combination of hardness, flexibility, flow, appearance, and superior resistance to dirt retention in indoor and outdoor applications. These coatings are highly resistant to abrasion, metal marking, staining, and marring, and require minimal maintenance. Glazetech uses polyester paints which provide excellent colour and gloss retention properties.

?

Polyvinylidene Fluoride Coatings (PVDF)
? ? PVDF (polyvinylidene fluoride) is a chemical resistant thick film barrier coating commonly used in architectural applications where both excellent appearance and substrate protection must be maintained over a long period of time. This coating is unaffected by most chemicals and solvents and has excellent wear and abrasion resistance. PVDF also has a high dielectric strength, excellent resistance to weathering and the ability to self extinguish.

?

- - - -
Category | Pre-coated abrasion-resistant
aluminum sheet | Acrylic pre-coated
aluminum sheet |
Coating thickness | 25um | 20um |
Pencil hardness | Breaking
Scratching | 7H
5H | 2H |
Coin scratch resistance | 5 points method | 5 | 3 |
MEK resistance | Load 0.5kg | >50 times | >50 times |
Glossiness | Reflectivity 60° | 20-40% | 10-80% |
Coating adhesion | Matrix Erichsen test | 100 / 100 | 100 / 100 |
Impact resistance | DuPont& acute;s drop impact test
1/2& quot;φ500g 50cm | No swelling, no peeling | No swelling, no peeling |
Bending workability | OT bend test |
Salt spray resistance | Salt spray test
5%Nacl 35°C 1000 hours |
Humidity resistance | 40°C, RH95% 1000 hours |
Boiling water resistance | 8 hours |
Chemical resistance | 24-hour immersion in
5%H2SO4 at room temperature | No color change | No color change |
24-hour immersion in
5%Hcl at room temperature |
24-hour immersion in
5%NaOH at room temperature |
- - - -

?

?

- - - -
Chemical composition% |
Grade | Si | Fe | Cu | Mn | Mg | Cr | Ni | Zn | Al |
1050 | 0.250 | 0.400 | 0.050 | 0.050 | 0.050 | - | - | 0.050 | 99.50 |
1060 | 0.250 | 0.350 | 0.050 | 0.030 | 0.030 | - | - | 0.050 | 99.60 |
1070 | 0.200 | 0.250 | 0.040 | 0.030 | 0.030 | - | - | 0.040 | 99.70 |
1100 | Si+Fe:0.95 | 0.05-0.2 | 0.050 | - | - | 0.100 | - | 99.00 |
1200 | Si+Fe:1.00 | 0.050 | 0.050 | - | - | 0.100 | 0.050 | 99.00 |
1235 | Si+Fe:0.65 | 0.050 | 0.050 | 0.050 | - | 0.100 | 0.060 | 99.35 |
3003 | 0.600 | 0.700 | 0.05-0.2 | 1.0-1.5 | - | - | - | 0.100 | remains |
3004 | 0.300 | 0.700 | 0.250 | 1.0-1.5 | 0.8-1.3 | - | - | 0.250 | remains |
3005 | 0.600 | 0.700 | 0.250 | 1.0-1.5 | 0.20-0.6 | 0.100 | - | 0.250 | remains |
3105 | 0.600 | 0.700 | 0.300 | 0.30-0.8 | 0.20-0.8 | 0.200 | - | 0.400 | remains |
3A21 | 0.600 | 0.700 | 0.200 | 1.0-1.6 | 0.050 | - | - | 0.10 | remains |
5005 | 0.300 | 0.700 | 0.200 | 0.200 | 0.50-1.1 | 0.100 | - | 0.250 | remains |
5052 | 0.250 | 0.400 | 0.100 | 0.100 | 2.2-2.8 | 0.15-0.35 | - | 0.100 | remains |
5083 | 0.400 | 0.400 | 0.100 | 0.40-1.0 | 4.0-4.9 | 0.05-0.25 | - | 0.250 | remains |
5154 | 0.250 | 0.400 | 0.100 | 0.100 | 3.1-3.9 | 0.15-0.35 | - | 0.200 | remains |
5182 | 0.200 | 0.350 | 0.150 | 0.20-0.50 | 4.0-5.0 | 0.100 | - | 0.250 | remains |
5251 | 0.400 | 0.500 | 0.150 | 0.1-0.5 | 1.7-2.4 | 0.150 | - | 0.150 | remains |
5754 | 0.400 | 0.400 | 0.100 | 0.500 | 2.6-3.6 | 0.300 | - | 0.200 | remains |
6061 | 0.40-0.8 | 0.700 | 0.15-0.40 | 0.150 | 0.8-1.2 | 0.04-0.35 | - | 0.250 | remains |
6063 | 0.20-0.6 | 0.350 | 0.100 | 0.100 | 0.45-0.9 | 0.100 | - | 0.100 | remains |
6082 | 0.7-1.3 | 0.500 | 0.100 | 0.40-1.0 | 0.6-1.2 | 0.250 | - | 0.200 | remains |
6A02 | 0.50-1.2 | 0.500 | 0.20-0.6 | Or Cr0.15-0.35 | 0.45-0.9 | - | - | 0.200 | remains |
8011 | 0.50-0.9 | 0.6-1.0 | 0.100 | 0.200 | 0.050 | 0.050 | - | 0.100 | remains |
- - - -

?

?

- - - -
Alloy | Wrought aluminum alloy composition limits (% weight) |
Si | Fe | Cu | Mn | Mg | Cr | Ni | Zn | ? | Ti | Zr | Limits?? | Al |
Each | Total |
1060 | 0.25 | 0.35 | 0.05 | 0.03 | 0.03 | — | — | 0.05 | V:0.05 | 0.03 | — | 0.03 | — | 99.6 |
1100 | Si+Fe :0.95 | 0.05~0.20 | 0.05 | — | — | — | 0.1 | ? | — | — | 0.05 | 0.15 | 99 |
3003 | 0.6 | 0.7 | 0.05~0.20 | 1.0~1.5 | — | — | — | 0.1 | — | — | — | 0.05 | 0.15 | Remainder |
8011 | 0.50~0.9 | 0.6~1.0 | 0.1 | 0.2 | 0.05 | 0.05 | — | 0.1 | — | 0.08 | — | 0.05 | 0.15 | Remainder |
? Mechanical Properties Tensile strength σb(MPa) ≤ 145 Elongation δ10 (%): ≥ 12 |
- - - -

?