MoSi2 Molybdenum Products Molybdenum Heating Elements for Disilicide Furnace?
?
Product Description
?
MoSi2 heating elements is made from Molybdenum Disilicide with excellent thermal resistance.?It can be used in air and various gases environments. Working temperature of MoSi2 heating element is 1300C to 1800C and it?has been widely used as heaters in high temperature furnaces and kilns of metallurgy, glass, ceramic refractory, crystal electronic device, industrial furnace manufacture and chemical industry field.
?
Types of MoSi2 Heating Elements
1. According to temperature: 1700C and 1800C
2. According to Shape: U, W, I, UL, WL, Spiral types.
?
MoSi2 Heating Elements Standard Size:
(Hot zone dia / Cold zone dia)
3/6mm, 4/9mm, 6/12mm, 9/18mm, 12/24mm.
?
Chemical property of MoSi2
High temperature oxidation resistance:
When MoSi2 heating elements are used at high temperature and under oxidation circumstance, a dense layer of quartz (SiO2) is generated on the surface of the element to prevent it from further oxidation.
When the temperature of element is over 1700oC, the SiO2 protecting film whose melting point is 1710oC will be melted. Due to its surface tension, SiO2 agglomerate() into drops and lose protection. The SiO2 protecting film is formed again when the element continues to be used under the oxidation circumstance.
It must be pointed out is that the MoSi2 heating element cannot be used in the temperature between 400oC to 700 oC for long time. Otherwise, the element will be pulverized because of the strong low-temperature oxidation.
?
Resistance characters
?
MoSi2 heating elements have good resistance characteristic, so it is an ideal heating material to replace traditional heating elements.
?
At room temperature, its resistivity is very low, with the increase of temperature, the resistance increases sharply. The advantages of heating up fast and low power consumption are obvious.?
?
In normal operating circumstances, the resistance of the element is constant, so the old and new components can be mixed.
??
Molybdenum MoSi2 Heating Elements& acute; Application:
?

- - - -
Item | Name | Distinction criterion | Specification | Using range |
Heating elements | 1700? type | Element operating temperature 1700oC?is acceptable | Le Φ
6-12W type/U type/L type/all kinds of hetero type / stripe shape | high temperature electric resistance furnace |
1800? type | Element operating temperature 1800oC?is acceptable |
1800J type | Element operating temperature≥1800oC | Le Φ
3-12W type | Special,high temperature and high-power electric resistance furnace |
1800T type | Element operating ?temperature≤1800oC | Le Φ
3-12W type U type | Not oxidized special air high temperature electric resistance furnace |
- - - -

?
Atmosphere influence on the MoSi2 heater& acute;s operating temperature:?
?

- - - -
Atmosphere | The max element temperature(oC) |
? | 1700type | 1800type |
Air | 1700 | 1800 |
N2? | 1600 | 1700 |
He ?Ar? Ne ?Argon, Helium | 1600 | 1700 |
Dry Hydrogen(dew point) -80oC | 1150 | 1150 |
Wet Hydrogen(Dew point) -20oC | 1450 | 1450 |
mixed gas(e . g . 10%CO2, 50%CO, 15% H2) | 1600 | 1700 |
mixed gas(e . g . 40%CO2 , 20%CO) | 1400 | 1450 |
Cracked and partly burnt ammonia? | 1400 | 1450 |
- - - -

?
Physics Characters of MoSi2
?

- - - -
Bulk density | Bending strength | Hardness | Apparent porosity | Drawing water rate | Thermal elongation rate |
5.6~5.8g/cm3? | 20MPa(20oC) | (hv)570kg/mm2 | 0.5~2.0% | 0.5% | 4% |
- - - -

?
Recommend surface load:
?

- - - -
Furnace Temp(°c) | 1400 | 1500 | 1600 | 1650 | 1700 |
Surface load of hot zone(W/cm2) | <18 | <15 | <12 | <10 | <8 |
- - - -

?