JH-9088 Zinc Flake Coating , High Corrosion Resistance Nanometer Alloy Coating

?

?

1?Product?Information

?

?

According?to?the?galvanized?coating?have?poor?corrosion?resistance?and?defect?of?acid?and?alkali?resistant,our?

companyI?developed?JH-9088?high?corrosion?nano?alloy?coatings.It?can?improve?the?corrosion?performance?of?the?

coating,make?the?salt?spray?time?increased?to?more?than?1000?hours,?but?also?increase?the?hardness,?acid?and?

alkali-resistant?on?the?coating?surface,?and?the?surface?color?can?be?diversified.?

?

?

2?Composition/information?on?ingredients

?

?

The?basic?materials?of?this?product?is?nano-alloy?powder,?toughening?agents,?film?formers,?organic?solvents?and?

color?paste,?adding?other?additives?mixed.?

?

?

3?Performance?Characteristics

?

?

This?product?can?be?use?by?dipping?and?spraying?ways?to?treat?on?galvanized?parts,?parts?surface?treated?uniformly,

?no?blind?spots.?The?treated?parts,anti-corrosion?ablity?is?ten?times?exceed?galvanized?workpieces,?salt?spray?time?increased?to?more?than?1000?hours.?

And?have?excellent?heat-resistant?and?antiacid,?anti-alkali,anti-salt?and?other?properties,?its?smooth?surface,?high?

hardness,?anti-scratch,?color?can?meet?the?needs?of?the?deployment.

?

?

4?Market?Application

?

?

This?product?is?suitable?for?long-term?corrosion?protection?for?outdoor?galvanized?parts.?Such?as?railway?fasteners,

?bridges,?buildings,?power?communications?fasteners,?etc.

?

?

5?Construction?Method?and?Attention

?

?

5.1?This?product?can?use?spraying?and?dipping?ways?for?coating.

5.2?Fully?stirring?before?use,?should?use?special?diluent?to?adjust?viscosity.

5.3?Add?centrifugal?procedure?for?dipping?process.

5.4?Cleaning?appliance,?use?alcohol?or?ether?organic?solvents

?

?

6?Packing,Storage,Transportation

?

?

Packing:Steel?drum,Net?weight:20kg/drum(can?also?according?to?customer& acute;s?requirement).

Storage:Tightly?closed,below?40℃,keep?in?indoor?places,?without?direct?sunlight

Transportation:Should?prevent?rain,?sun?exposure,?and?shall?comply?with?the?relevant?provisions?of?the?transport?

sector.

?

?

7?Coating?process

?

?

7.1?Process?flow

?

Galvanized?parts?dipping?Spraying?Pre-curing,Curing?Inspection?&?Packing

?

7.2?Process?parameters

?

Dipping:Room?temperature,density:30-45s.

????????Centrifuge?dripping:210-270/min,30-60s

Spraying::Room?temperature,density:25-35s.

?

7.3?Curing?Condition

?

Pre-curing:Temperature:80-150℃,10-15min,choose?whether?pre-curing?depend?on?the?thickness?of?the?workpiece.

Curing:Temperature:200-220℃,20-30min,?box-type?furnace?or?channel?devices?both?ok.

?

?

8?Technical?Data

?

?

- - - -
NO | Item | Inspection?Standard | Remark |
1 | Apperance | Silver?Coating?liquid | ? |
2 | Density | 0.9-1.2g/ml | 50ml?hydrometer?jar |
3 | Viscosity | 25-45s | ? |
4 | Diluent | Use?diluent?djust?to?the?coating?viscosity | JH-9088B?Diluent |
- - - -

?

?

9?Coating?Liquid?Viscosity?and?The?Amount?of?Diluent?Synopsis

?

?

- - - -
NO | Coating?Liquid?(g) | Diluent?(g) | Density?(s) |
1 | 100 | 0 | 80 |
2 | 100 | 3.5 | 56 |
3 | 100 | 6.5 | 45 |
4 | 100 | 10 | 38 |
5 | 100 | 11.5 | 35 |
- - - -