High Wear Steel Heat Resistance Castings For Furnaces With 1300 Degree DF019 - DF019
High Wear Steel Heat Resistance Castings For Furnaces With 1300 Degree DF019 For Sale, Most Competitive Price, Fast Delivery, Custom Service, Wholesale High Wear Steel Heat Resistance Castings For Furnaces With 1300 Degree DF019, Made in China, High Quality Products!, China cheap prodocuts, china suppliers Supplier, Manufacturer.
High Wear Steel Heat Resistance Castings For Furnaces With 1300 Degree DF019?
?
?
Quick Details
High Wear Resistance Castings?Feature:
1. Different temperature ranges within 600~1300.
2. Applications:spraying nozzles of boilers, grate bars for sintering, ......
High Wear Resistance Castings?Description:
A. Highly alloy heat and abrasion resistant castings can effectively resist heat, wear and oxidation in different temperature ranges within 600~1300.
B. The main products include spraying nozzles of boilers, grate bars for sintering, grate plates for clinker cooling machines, furnace bed plates and teeth for slag crushers.
- - - -
Material | Endurance strength(Mpa)
1000 1000hr | Oxidation weight gain (g/m2)
1000 500hr | Temperature range applicable |
30Cr26Ni14Si2MoNRENb | ≥16 | ≤50 | 800~1300 |
40Cr25Ni20 | ≥10 | ≤50 | 800~1300 |
35Cr18Ni25Si2 | ≥8 | ≤65 | 800~1300 |
30Cr22Ni4Mn4Si2N | ≥8 | ≤115 | 600~1300 |
Cr26 cast iron | high wear resistance | ≤100 | 600~1300 |
- - - -
?
China heat-resistant castings supplier provides heat resistant casting services to worldwide heat resistant castings customer. Hope you find our heat resistant steel casting process and heat resistant cast steel product description helpful.
?
In the recent 20 years, our liners have been widely used in large, medium and small ball mills in Chinese power generation, mining, cement, Chemical engineering and metallurgical industries and super fine pulverizing equipments. It is the only recommended liner product in the latest standard of the electric-power industry in China.
Technical Parameters
Wuxi Orient Anti-wear Engineering Co., Ltd.
Chemical Composition & Mechanical Property of Wear-resistant Castings
- - - -
Item | Cr-Mo Alloy Steel I | Cr-Mo Alloy Steel II | Cr-Mo Alloy Steel III | High Cr white iron | High Cr Alloy Steel | High Manganese Steel | Ni-Hard cast iron |
C | 0.30~0.50 | 0.65~0.90 | 0.40~0.90 | 2.40~3.20 | 1.1~2.2 | 0.90~1.30 | 2.40~3.60 |
Si | 0.50~1.20 | ≤0.75 | 0.70~1.20 | 0.60~1.20 | 0.60~1.20 | ≤0.08 | ≤0.80 |
Mn | 0.40~1.20 | 0.50~1.20 | 0.60~1.00 | 0.50~1.00 | 0.50~1.00 | 11.00~18.00 | ≤2.0 |
Cr | 1.70~2.50 | 1.50~2.50 | 4.00~7.00 | 12.00~30.00 | 11.00~30.00 | 1.50~2.50 | 1.5~10 |
S | ≤0.04 | ≤0.06 | ≤0.04 | ≤0.04 | ≤0.04 | ≤0.04 | ≤0.15 |
P | ≤0.04 | ≤0.06 | ≤0.06 | ≤0.06 | ≤0.06 | ≤0.06 | ≤0.15 |
Mo | ≤0.5 | ≤0.5 | ≤0.5 | 0.10~3.0 | 0.10~3.0 | ≤1.0 | ≤0.10 |
Cu | 0.10~0.60 | ≤0.25 | 0.20~0.40 | 0.10~1.00 | 0.10~1.00 | - | - |
Ni | ≤0.50 | ≤0.30 | 0~0.30 | 0~0.30 | 0~0.30 | - | 3.3~10 |
Re | ≤0.02 | ≤0.02 | ≤0.02 | - | - | - | - |
Equivalent Specifications | DL/T 681-1999 ? GB/T26651-2011 | AS 2074 L2B Mod | DL/T 681-1999 | GB/T 8263-1999 AS 2027 Cr27 AS 2027 CrMo 15/3 AS 2027 CrMo 20/2/1 ASTM A532 Class III type A 25% Cr ASTM A532Class II type B 15% Cr-Mo BS 4844 3E DIN1695 NFA32401. | GB/T 5680-1998 DL/T 681-1999 JIS G 5153-1999 ASTM A 128 DIN GX120Mn12 AFNOR:Z120Mn12 | GB/T 8263-1999 AS 2027/Ni-Cr1-550 AS 2027/Ni-Cr2-500 AS 2027/Ni-Cr4-500 AS 2027/Ni-Cr4-600 AS 2027/Ni-Cr4-630 ASTM A 532 1-A,B,C,D ASTM A 532 2-A,B,C,D,E ASTM A 532 3-A |
Material Type | Martensite Steel | Martensite or Pearlitic Cr Mo Steel | Martensite Steel | Martensite matrix | Austenitic Mn Steel | - |
Hardness | HRc≥48 | HB470 & HB 321~370 | HRc≥50 | HRc≥56 | HB≤300 | HRc≥56 |
Impact Value | Ak≥40J | - | Ak≥10J | Ak≥4J | Ak≥80J | - |
- - - -
?
?
?
?
?
?
?
?
?
?
?
?
?
?
?
?
?
?
?
?
?
?
?
?
?
?
?
?
?
?
?
?
?
?
?
Our foundry has complete melting, heat treatment and test equipments, such as mid-frequency induction electrical furnaces, quenching and tempering furnaces, blast shot, spectrometer, Rockwell and Brinell Hardness tester, impactor, UT tester and metallographic microscope. We achieved the certificate of quality management system ISO 9001:2008. We have been exporting castings to oversea markets, such as Brazil, Australia and South Africa.
Foundry Photo
?
Wuxi Orient Anti-wear Engineering Co.,Ltd
Address: Zhongyao,Xishan District, Wixi, Jiangsu, China, 214000
Tel: 86-510-88798440
Wuxi Orient Anti-wear Engineering Co., Ltd.
We specialize in production of wear, heat and corrosion-resistant castings and the relevant grinding equipments. We were awarded the certificate of High New Technology Enterprise issued by Sci-tech Bureau, Jiangsu Province in 2004.
We possess famous patented product----COMBINED SELF-FASTENED (BOLTLESS) BALL MILL LINERS, called "China Best Liner", which was invented under the guidance of the 鈥淪ystem Engineering Theory of Ball-Mills鈥? which was proposed by General Manager, Senior Engineer, Mr. Chen Changshun. The lining plates, without any bolts, are easily installed. The plates are firmly assembled and easily maintained under a low cost. This is an epoch-making ball mill liner product in the past 100 years. The reliability and stability of the new plates are much better than those of traditional bolted ones. In the recent 20 years the boltless ball mill liners have been widely used in large, medium and small ball mills in coal-fired power plants, mines, cement works, chemical engineering factories and super fine powder grinding plants. It is the only recommended liner product which is allowed to be list into the latest Electrical Power Industry Standard in China (DL/T681-1999). The product was awarded the certificate of High New Technology Product, issued by Sci-tech Bureau, Jiangsu Province in 2004.
Our products involve various kinds of materials, such as low Chrome alloy steel, middle Chrome alloy steel, high Chrome alloy steel, high chromium white iron, low chromium cast iron, Ni-hard cast iron, high Manganese steel and other heat and corrosion-resistant castings.