Rubber & Products

INTRODUCTION:
It is a hydrophilic addition silicone rubber impression material, it contains two components, Part A is platinum catalyst, and Part B is hydrogen containing polysiloxane. This product comprises liquid material and powder material. The main raw material is a silicone oil, silicone resin, alumina, quartz powder and etc.

COMPOSITION:
Base components 350 g;
Catalyst component 350 g;
A white spoon;
A blue spoon

PHYSICAL PROPERTIES:
Appearance:Catalyst Components(White putty),
Base Components(Blue putty);
Mix ratio: 1:1
Pot life: > 60 seconds
Curing time(37C):< 5 min
Hardness(S** A):60
Permanent deformation (%):<0.2
Dimensional stability (%):<0.25
Copy details(μm): <1.5
Tearing Strength (Mpa):2.0
Temperature stability: 60°C for 1 week
Elongation(%):267

APPLICATION:
It is suitable for the production of precise dental crown, dental fixed bridge, dentures, and articulation registration and takes the mold of ** tissue

USAGE INSTRUCTION:
1. Under the room temperature, take the same amount of base component (blue) and catalyst component (white).
2. Mix the two components together. It is recommended to use the blue spoon to take the base component and white spoon to take catalyst component.
3. Use your fingertips to mix the two components together and knead for at least 30 seconds until they are mixed completely.
4. Close the lid immediately after usage, the cover can not be interchanged.

MAIN FEATURE:
1. Good plasticity, small volume incorporation rate, it needs only 3-5min to vulcanize into elastomer at ** temperature, very easy to remove from the mouth after the stamp, and has good chemical stability.
2. High accuracy of mold impression, capability of reproducing the fine structure of the mouth, with good elastic recovery, and good tear strength and dimensional stability, it can provide accurate and reliable morphological basis for clinical dentistry.