K10 Tungsten Carbide Rod Blanks with 6% Cobalt , High Hardness tungsten carbide metal

AIA-1

Send Inquiry

Description

K10 Tungsten Carbide Rod Blanks with 6% Cobalt, Hardness 93.5 - 93.8 HRA

?


Description:?

?

Cemented carbide essentially consists of two main components: hard metal tungsten carbide (WC) and binding agent Co. Carbide contributes to high hardness property in a most important degree for hard metal WC, while cobalt maintains its relative high toughness at the high level of hardness. With Hot Isostatic Pressing sintering technique, cemented carbide material is fully consolidated by simultaneous application of heat and pressure, producing a close-to-full-density state. Consequently, the technique greatly optimizes rod’s quality, being more stable and reliable.?

?

- ISO Range: K10

?

- with 94% tungsten carbide, 6% cobalt?

?

- Made of 0.4 micron ultrafine TC powder

?

- Hardness: 93.5-93.8 HRA

?

- Bending strength: >3200 MPa

?

- Density:?14.8 g/cm3

?

- As sintered
? ? ? ? ? ? ? ? ? ? ? ? ? ? ? ? ? ? ? ? ? ??
- Dimension: unground fixed length bar in metric size


?

Specifications:

?


?

Solid?rods-?cut?to?length(Metric):

?

- - - -
D | Tolerance?of?D | Length | D | Tolerance?of?D | Length |
mm | (mm) | mm | mm | (mm) | mm |
3.0 | +0.2/+0.4 | 38.5 | 8.0 | +0.2/+0.4 | 100 |
3.0 | +0.2/+0.4 | 50 | 8.0 | +0.2/+0.4 | 150 |
3.0 | +0.2/+0.4 | 60 | 9.0 | +0.2/+0.4 | 100 |
3.0 | +0.2/+0.4 | 75 | 10.0 | +0.2/+0.4 | 75 |
3.0 | +0.2/+0.4 | 100 | 10.0 | +0.2/+0.4 | 120 |
4.0 | +0.2/+0.4 | 50 | 10.0 | +0.2/+0.4 | 150 |
4.0 | +0.2/+0.4 | 60 | 10.0 | +0.2/+0.4 | 200 |
4.0 | +0.2/+0.4 | 75 | 11.0 | +0.2/+0.4 | 100 |
4.0 | +0.2/+0.4 | 100 | 12.0 | +0.2/+0.4 | 75 |
5.0 | +0.2/+0.4 | 50 | 12.0 | +0.2/+0.4 | 100 |
5.0 | +0.2/+0.4 | 60 | 12.0 | +0.2/+0.4 | 120 |
5.0 | +0.2/+0.4 | 75 | 12.0 | +0.2/+0.4 | 150 |
5.0 | +0.2/+0.4 | 100 | 14.0 | +0.2/+0.4 | 75 |
6.0 | +0.2/+0.4 | 50 | 14.0 | +0.2/+0.4 | 150 |
6.0 | +0.2/+0.4 | 75 | 16.0 | +0.2/+0.4 | 100 |
6.0 | +0.2/+0.4 | 100 | 16.0 | +0.2/+0.4 | 150 |
6.0 | +0.2/+0.4 | 150 | 18.0 | +0.2/+0.4 | 100 |
6.0 | +0.2/+0.4 | 60 | 20.0 | +0.2/+0.4 | 100 |
8.0 | +0.2/+0.4 | 75 | 20.0 | +0.2/+0.4 | 150 |
- - - -

?
?


?

Areas?of?Application:

?

We would be glad to advise you when choosing the grades to suit optimally your requirements. Following are applications that our HF06(K10) fits for cutting.?


1. Grey cast Iron
2. Unalloyed steels
3. Plastic

?

?

Competitive Advantage:

?

Compared to high speed steel, tungsten carbide consists of natural hard and stable phase, and practically doesn’t lose any level of its high hardness when heating up. However, the high hardness of HSS is only in a result of quenching process during which hard phase nucleates & grows. It breaks down easily when annealing. Therefore, carbide tools last significantly longer than HSS. ?
? ??
Quality can be taken for granted. We have been producing tungsten powder, tungsten carbide powder FOR 11 years, being famous for its quality and winning high reputation within China. As so, each pre-process for making solid rods is clearly and strictly monitored. Thus, the quality of solid TC rods is guaranteed to be high and stable.?